Comunicare con Fornitore? Fornitore
LIU Mr. LIU
Cosa posso fare per te?
Contattare il Fornitore

XUCHUAN CHEMICAL(SUZHOU) CO., LTD

  • materiale in resina poliuretanica per colata sandali con cinturini
  • materiale in resina poliuretanica per colata sandali con cinturini
  • materiale in resina poliuretanica per colata sandali con cinturini
  • materiale in resina poliuretanica per colata sandali con cinturini
  • materiale in resina poliuretanica per colata sandali con cinturini
  • materiale in resina poliuretanica per colata sandali con cinturini

materiale in resina poliuretanica per colata sandali con cinturini

Payment Type:
L/C,T/T
Incoterm:
FOB,CIF
Min. Order:
17600 Kilogram
Delivery Time:
15 Days
Transportation:
Ocean,Land
Port:
Shanghai
Share:
  • Descrizione del prodotto
Overview
Product Attributes

ModelloA-9088W,B-6088

marchioXuchuan Chemical

Supply Ability & Additional Informations

Pacchetto220 kg / fusto

produttività260000tons/month

TrasportiOcean,Land

Luogo di origineCina

PortaShanghai

Tipo di pagamentoL/C,T/T

IncotermFOB,CIF

Termine di consegna15 giorni

Confezionamento e consegna
Unità vendibili:
Kilogram
Tipo pacchetto:
220 kg / fusto
DESCRIZIONE DEL PRODOTTO

Materiale in resina poliuretanica per stampaggio in PU per sandali con cinturini

Dettagli del prodotto

Application shoe sole
Keywords pu molding,polyurethane resin for casting,material straps for sandals
A/B Materials Temperatures(℃) A/B Materials Temperatures(℃)
A+C/B Mix ratio (By weight) 100/100~102
Cream Time (s) 6~8
End of Rise Time (s) 30~40
Free Rise Foam Density(g/cm3) 0.21~0.26
Mold Temperature(℃) 45~55
Demold Time(min) Demold Time(min)
Molded Density (g/cm3) 0.35~0.60

Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line

Application: Outsole, slippers, wedge shoes

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density (g·cm-3/40)

Package(kg)

/

/

/

A-9080W

Cream,White,liquid

1000~1300

1.01~1.02

18

/

/

/

B-6088

Yellowish transparent liquid or waxy

600~800

1.08~1.2

20

/

/

/

Materials preheat

A-9080W:  preheated at 50~60 for 6~8 hours.

B-6088:    preheated at 50~60 for 6~8 hours.

Typical processing parameters & Reaction parameter.

Items

A/B Materials Temperatures()

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature()

Demold Time(min)

Parameter

40~45/38~42

100/100~102

6~8

30~40

0.21~0.26

45~55

5~7

The adding content of C-2 should be 210g±10g/18kg.

The adding content of water should be 0~80g/18kg according to the reality.

The adding content of hardener should be 0~1200g/18kg according to the reality.

Physical properties

Items

Molded Density (g/cm3)

Hardness
(Shore A )

Tensile strength
(MPa)

Elongation
(%)

Tear Strength
(kN/m)

Williams abrasion
(cc/php)

/

Physical  properties

0.35~0.60

60~88

4~7

200~300

11~20

130~200

/

Demold time may be prolonged with the increase of sole thickness.

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


PROFILO AZIENDALE

PROCESSO PRODUTTIVO
CERTIFICAZIONE
IMBALLAGGIO E SPEDIZIONE
FAQ

CONTATTACI

Elenco prodotti : Sistema in poliuretano per suola di scarpe > Sistema in poliuretano per sandali e pantofole

Mail a questo fornitore
  • *A:
    Mr. LIU
  • *messaggio:
    Il tuo messaggio deve essere compreso tra 20-8000 caratteri

Elenco prodotti correlati

Casa

Product

Phone

Informazioni aziendali

inchiesta