Comunicare con Fornitore? Fornitore
LIU Mr. LIU
Cosa posso fare per te?
Contattare il Fornitore

XUCHUAN CHEMICAL(SUZHOU) CO., LTD

  • Resina PU impermeabilizzante alifatica per gommapiuma
  • Resina PU impermeabilizzante alifatica per gommapiuma
  • Resina PU impermeabilizzante alifatica per gommapiuma
  • Resina PU impermeabilizzante alifatica per gommapiuma
  • Resina PU impermeabilizzante alifatica per gommapiuma
  • Resina PU impermeabilizzante alifatica per gommapiuma

Resina PU impermeabilizzante alifatica per gommapiuma

Payment Type:
L/C,T/T
Incoterm:
FOB,CIF,EXW
Min. Order:
17600 Kilogram
Delivery Time:
15 Days
Transportation:
Ocean,Land,Air
Port:
Shanghai
Share:
  • Descrizione del prodotto
Overview
Product Attributes

ModelloA-3070,B-8280

marchioXuchuan Chemical

Supply Ability & Additional Informations

Pacchetto220 kg / fusto

produttività260000tons/month

TrasportiOcean,Land,Air

Luogo di origineCina

PortaShanghai

Tipo di pagamentoL/C,T/T

IncotermFOB,CIF,EXW

Termine di consegna15 giorni

Confezionamento e consegna
Unità vendibili:
Kilogram
Tipo pacchetto:
220 kg / fusto
DESCRIZIONE DEL PRODOTTO

Resina PU poliuretanica liquida impermeabilizzante alifatica per gomme espanse

Dettagli del prodotto

Application Industrial tyre wheel
Product name Polyurethane
A/B Materials Temperatures(℃) 40~45/38~42
A+C/B Mix ratio (By weight) 100/101~103
Cream Time (s) 8~10
End of Rise Time (s) 60~70
Free Rise Foam Density(g/cm3) 0.24~0.26
Mold Temperature(℃) 45~55
Demold Time(min) 5~7

Characteristic: Good handle, smooth surface

Application: Tire

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density (g·cm-3/40)

Package(kg)

/

A-3070

Liquid

1000~1400

1.01~1.02

18

B-8280

Yellowish transparent liquid or waxy

800~1200

1.08~1.2

20

Materials preheat

A-3070:  preheated at 50~60 for 6~8 hours.          

B-8280:  preheated at 50~60 for 10~12 hours.

Typical processing parameters & Reaction parameter

Items

A/B Materials Temperatures()

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature()

Demold Time(min)

Parameter

40~45/38~42

100/101~103

8~10

60~70

0.24~0.26

45~55

5~7

The adding content of C-2 should be 250g±10g/18kg

The adding content of water should be 0~90g/18kg according to the reality

The adding content of hardener should be 0~600g/18kg according to the reality

Physical properties

Items

Molded Density
(g/cm3)

Hardness
(Shore A )

Tensile strength
(MPa)

Elongation
 (%)

Tear Strength
(kN/m)

 

 

 

 

Physical  properties

0.50~0.70

55~68

7.5~9.0

340~450

24~33

 

 

Demold time may be prolonged with the increase of sole thickness.

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


PROFILO AZIENDALE

PROCESSO PRODUTTIVO
CERTIFICAZIONE
IMBALLAGGIO E SPEDIZIONE
FAQ

CONTATTACI

Elenco prodotti : Sistema in poliuretano per suola di scarpe > Sistema in poliuretano per sandali e pantofole

Mail a questo fornitore
  • *A:
    Mr. LIU
  • *messaggio:
    Il tuo messaggio deve essere compreso tra 20-8000 caratteri

Elenco prodotti correlati

Casa

Product

Phone

Informazioni aziendali

inchiesta